Sheet Metal Flower to Practice Plasma Cutting and Welding

The purpose of this flower is to allow experience using a plasma cutter and MIG welding such that ugly novice cutting/welding adds to the charm of the flower.  Since practicing tends to make us focus on what we're not good at, why not use it to our advantage and have the outcome look better with uneven cuts and welds.

To make this flower, you will use the techniques in How to Use a Plasma Cutter and Basics of MIG Welding.

I made this at TechShop Detroit (www.techshop.ws).

This worked well because I really liked how the yellowish tinge of the scrap metal would contrast with the discoloration from cutting and welding.

The size of the petals can be completely subjective.  Note that the uneven cuts are due to lack of experience smoothly moving the plasma cutting gun across the surface.  When moving too fast the material is not cut all the way through.  Luckily, the uneven cuts work to your advantage here.

It is much better to start the cutter a little off the material and come in to cut.  To activate the plasma cutter, lift the safety and pull the trigger.

Note that I originally chose four petals but added another when I realized it was not  aesthetically pleasing enough.

Since you are a novice plasma cutter, your petals will likely be attached it a few locations.  Use pliers to gently remove the petal by gently bending the petal back and forth.  It is unlikely you will need excessive force.  Use the plasma cutter to make further cuts if you cannot move the petal.

As mentioned, in this case I cut four petals and decided that adding a fifth looked better.

Use a straight edge to guide the plasma cutter in a straight line for the stem.  In this case I used an angle that was lying around in the shop.  Make one cut and another parallel cut 

This is a tricky cut because you are starting within the material and do not have the option of coming in from the side with the gun already engaged.  Cut a circle as best you can and leave a sliver attached so that it doesn't fall through the grate.  

"Punch" it out from underneath and use the pliers to gently move it back and forth to remove from the material.

Set it among the other parts to ensure sizing is appropriate.

To set up this scenario, I chose to use 90 degree welding magnets.  I set up all five petals on five magnets, overlapping the petals in locations where they could be welded to each other.

Test the center circle and make sure that it sits within the petals, then remove it.

Weld the petals together.  Remember, even if the welds are not pretty the purpose of this is to practice.  Ugly welds will still make a beautiful flower.

Remove the welded petals from the magnets and ensure that the welds hold all petals together.

Test the center circle within the petals and welds.  Put the the center circle face down on a magnet.  Put the welded petals upside-down over the center circle. Place in most favorable position - the magnet holds all pieces together loosely.  Weld the petals to the center circle.

Use pliers to bend petals back to open flower.

Place the petals upside-down on the magnet.  Place the stem in the proper position behind the flower and position magnets to achieve the desired height.  Weld the stem to the back of the petals.

I used a basic picture hanger to display as an accent on my brick wall.